Niobium-Zirconium (Nb-Zr) alloys refer to the alloys composed of zirconium added to metal niobium, and it is regarded as a low-strength alloy. The alloys in general are inconvenient to weld. Both sides of the weld must be protected with a stream of inert gas, because hot niobium will react with oxygen and nitrogen in the air. The addition of 1% zirconium to niobium greatly improves the creep strength over the soft pure metal. Thus, Nb99Zr1 can replace pure niobium in applications requiring the chemical resistance of niobium and a material with high melting temperature.
Alfa Chemistry provides high-quality niobium-zirconium Wires which is worked from ingot to final diameter, furnished in coils or on spools or reels at a competitive price, which can be used in the welding industry or nuclear industry, and so on.
General Properties
Items | Niobium / Zirconium - Wire |
---|---|
Catalog | ACAM-Nb-A009 |
Material | R04261 (Nb99Zr1) |
Size | Diameter: 0.01"-0.124" (+/-0.002"), Length: On Request (Plus Tolerance) |
Standard | ASTM B392 |
Chemical Component
Elements | C | N | O | H | Zr | Ta | Fe | Si | W | Ni | Mo | Hf | Ti |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
R04621 | 0.01 | 0.01 | 0.025 | 0.0015 | 0.8-1.2 | 0.5 | 0.01 | 0.005 | 0.05 | 0.005 | 0.05 | 0.02 | 0.03 |
* Unit: %, max
Physical Properties
Grade | R4261 |
Ultimate Tensile Strength, Min, psi (MPa) | 28000 (195) |
Elongation min % | 15 |
Applications
In addition to greatly increasing the strength of pure niobium at higher temperatures, Nb99Zr1 also has low thermal nuclear capture cross-section properties. Furthermore, Nb99Zr1 has the advantage of being less expensive than the higher strength alloys. It can be used in applications where a high temperature material is needed with low loads. Its application areas can be summarized as follows:
- Nuclear industry
- Chemical industry
- Aviation and aerospace
- Mechanical manufacture